A. Tahiri ^{*}, M Idiri, A Hasnaoui and B Boubeker

Laboratoire d'Ingénierie et Matériaux (LIMAT), Faculté des Sciences Ben M’Sik Casablanca, Université Hassan II, Casablanca, Maroc

- *Corresponding Author:
- A. Tahiri

Laboratoire d'Ingénierie et Matériaux (LIMAT)

Faculté des Sciences Ben M’Sik Casablanca

Université Hassan II, Casablanca, Maroc

**Tel:**0665889572

**Email:**abl.tahiri@gmail.com

**Received Date**: 18/12/2017; **Accepted Date:** 27/02/2018; **Published Date**: 05/03/2018

DOI: 10.4172/2321-6213.1000213

**Visit for more related articles at** Research & Reviews: Journal of Material Sciences

In this work we performed a series of nanoindentation test on nanocrystalline (nc) tungsten (W) specimens, using Molecular Dynamics (MD) simulations and Embedded Atom Method (EAM). We studied the grain size effect in the range of 6 to 15 nm, with a penetration rate of 5 Å/ps and at room temperature 300 K. We found an increase in reduced elastic modulus Er and the Young elastic modulus E with the increase in grain size. On the other hand, we investigated the effect of the penetration velocity ranging from 3 Å/ps to 5 Å/ps. We found that the elastic modulus increases when the rate of penetration increases. The found results are in good agreement with the literature

Nanoindentation, Nanocrystalline tungsten, Molecular dynamics simulations, Grain size, Indenter velocity

Nanocrystalline materials, with grain size less than 100 nm, are known to possess some attractive properties, such as high yield and fracture strengths [1], improved wear resistance [2]. A lot of applications of nanocrystalline materials depend on grain size and temperature. Hariss [3] studied mechanical properties of polycrystalline tungsten at temperature ranging from 25°C to 950°C using nanoindentation. This method is widely used to obtain the elasticity modulus, hardness, and yield stress of nanocrystalline materials [4-7]. Nanoindentation is a method that uses an indenter with a known geometry to drive into a specific site of the specimen by applying an increased load [8,9]. This method is widely used for measuring mechanical properties of thin films, because it employs small loads (in the order of nanonewtons) that enable handling thicknesses at the nanometer scale. Recently some works are carried out using Finite Element (FE) nanoindentation simulation to study mechanical properties of thin films and coated systems [10,11]. Because of the development of computer simulation technology, the simulation scale expended from thousands to millions of atoms. Molecular Dynamics (MD) simulation has been used extensively to study material properties in various fields such as bioscience, chemistry, material science and technology [12,13]. Hasnaoui et al. [14] studied interaction between dislocations and grain boundaries under an indenter. Kelchner et al. [15] found that initial partial dislocation loops were nucleated off the indenting axis below the Au(111) surface. Ruestes [16] has studied the effects of indenter diameter, penetration velocity and interatomic potentials on defect mechanisms and evolution of tantalum nanoindentation. Hagelaar [17] studied the formation and destruction of nanoindentation contacts in tungsten. According to Li, et al. [4], MD simulations have been used to study the plastic deformation initiated by the indentation process. Dislocation nucleation and pile-up are observed during nanoindentation of a single crystal iron. Moreover, the plastic deformation of nanocrystalline tantalum during nanoindentation is regulated by deformation twin in terms of surface topography [18]. The main goal of this work is to analysis these effects on nanoindentation of nc tungsten by using MD simulations. The results are compared in part with those proposed by other simulation methods but also with experience.

**Interatomic Potentials**

The MD simulation solves NewtonÃÂ¢Ãâ¬ÃÅ¸s equations of motion and gives the trajectory of each atom in each time. The forces on an atom are computed as negative gradients of the potential energy of each atom [19]. The source of this potential energy is the interatomic potential, which limits the physics of how atoms interact with each other, and can be considered as the critical component of an MD simulation. An interatomic potential uses the location of an atom relative to all of its neighbors to calculate its potential energy. The mathematical form of an interatomic potential is typically selected and then parameters are determined by fitting to experimental and quantum mechanical simulation data; for this reason, potentials are considered to be empirical [20]. The embedded atom method is currently a common technique used in molecular dynamics computer simulation of metallic systems [21]. The method provides a good description of the interatomic forces in the system, particularly for fcc metals. It calculates the interatomic potentials in metals and models forces between atoms as follows

(1)

Where E is the total energy of the system, V(r_{ij}) represents the pair interaction energy between an atom i and its neighboring atom j, φ(r_{ij}) is the electronic density function, and F(ρi) represents an embedding function accounting for the effects of the free electrons in the metal [22]. In particular, we used the EAM potential functions developed [23].

In this study, MD simulations are performed using the Large Scale Atomic/Molecular Massively Parallel Simulator code (LAMMPS) [24]. We use periodic boundary conditions in the lateral directions (x and y) and a free surface in the indenting direction (z). The sample sizes perpendicularly to the indentation direction were chosen to be large enough to avoid spurious effects of the periodic boundary conditions. We used a fixed boundary condition at the bottom of the nc-W, representing a hard substrate. The indenter is modeled by a virtual spherical indenter using a strong repulsive potential.

**Sample Preparation**

We start by constructing nanocrystals that contain 5 grains with anaverage grain size of 15 nm, 9 nm and 6 nm using the Voronoi construction [25]. The simulations box is a cube with dimensions corresponding to the average grain size. The heart of the grains contains atoms are ranging bcc lattice with random crystallographic orientations. The simulations were performed using a rigid spherical indenter with a radius of 30 Å. The indenter moved toward the surface of the sample at a constant velocity until the desired depth was reached and then the system was equilibrated for several simulation steps [26,27].

**Indentation Simulation Process**

In this work we use an indenter velocity ranging from 3 Å/ps to 5 Å/ps, which is much faster than in experiments [28], but although carried out with relatively higher speed these simulations could still reveal the main features of the atomic rearrangements [29]. The MD time step is set to 1fs. The sample was initially relaxed at 300 K using the velocity rescaling method [4]. The bottom 20 Å of the substrate are kept fixed; the region from 20 Å to 40 Å are set as the thermostat atoms and the top of the sample surface was treated as a free surface [30].

**Hertzian Contact**

**Figure 1** exhibits an example of the load curves that shows the load versus the indentation depth for a grain size of 15 nm. The indenter force was determined from an average of the instantaneous indenter force over the last 100 fs before the indenter is moved down. The force in hertzian theory is given by:

(2)

Where R stands for the radius of the indenter (30 Å), h is the indentation depth and E_{r} is the reduced elastic modulus of W, given by:

(3)

With E is the Young’s modulus and ϑ the PoissonÃÂ¢Ãâ¬ÃÅ¸s ratio. We note that the value of is taken to be 0.28 as given by the interatomic potential [26].

We can see from **Table 1** that the Young’s modulus increases with increasing of the grain size. On the other hand, the Young modulus value 399.3 GPa, found for the 15 nm grain size sample is close to that of bulk W (410 GPa) [31]. Kang et al. [32] obtained value of 323.6 GPa for the Young modulus by nanoindentation and nanoscratch experiments of polycrystalline tungsten. Hariss et al. [3] carried out experiments and found that the reduced elastic modulus value is 287 GPa for the temperature range from 25 to 800°C. At 300 K, we calculated reduced elastic modulus of the 6nm average grain size sample and found 318.1GPa. This result is very close to that found experimentally by Dylan et al. [33] (317 GPa).

**Table 1:** Values of reduced elastic modulus, Young’s modulus of nc-W.

Mechanical properties | 6 nm | 9 nm | 15 nm |
---|---|---|---|

Reduced elastic modulus (Er) in GPa | 318.1 | 334.6 | 433.3 |

Young modulus in GPa | 293.2 | 308.3 | 399.3 |

**Reduced Elastic Modulus**

We plotted the result of **Table 1** in **Figure 2** and observed that the reduced elastic modulus Er of nanocrystalline tungsten shows a linear relationship with the reciprocal average grain size 1/d. This behavior has been observed experimentally by Sanders et al. [34].

The linear relationship between E_{r} and 1/d may be a general feature for nanocrystalline metals in the average grain size ranging presented in this paper. When the average grain size decreases the atomic fraction in grains boundary will decrease because of the increase of atomic fraction in grains. This can be seen in **Figure 3**, which shows that the reduced elastic modulus increases almost linearly with increasing of the atomic fraction of grains. We can deduce that E_{r} and 1/d have a linear relationship, at least in the studied range of average grain size. Zhou and Nan [35] also found a linear relationship for nanocrystalline metals with body-centered cubic (bcc) structure [35].

It is important to study the effects of the velocities of the indenter on the mechanical behavior. The velocities of the indenter are varied from 35 Å/ps to 5 Å/ps, respectively. In **Figure 4**, we plotted an example of these curves for the penetration velocity of 5 Å/ps. We found that for 5 Å/ps, the slope of the load–depth curve (10 eV.Å^{-3}) is steeper than that for the 4 Å/ps (8.9 eV.Å^{-3}) and 3Å/ps (8.3 eV.Å^{-3}). This shows that the Young’s modulus increases with the penetration velocity. These results were also found for nc-Ni [28] and nc-Cu [36].

MD simulations have been used to study the effect of penetration velocity and grain size on reduced elastic modulus and Young’s modulus of nanocrystalline tungsten. The load-depth curve is in a good agreement with the modified Hertizian theory. The values of the reduced elastic modulus obtained agree well with experiment and finite element simulation results. The effect of indentation velocity showed that the reduced modulus Er increases as the penetration velocity increases. The reduced modulus Er shows a linear relationship with the reciprocal of average grain size 1/d for nanocrystalline tungsten. This behavior is explained by the increase of the fraction of grain boundary atoms when the grain size increases.

- Gleiter. Nanocrystalline Materials. Progr Mater Sci 1989;33:223-315.
- Farhat ZN, et al. Effect of grain size on friction and wear of nanocrystalline aluminum. Mater Sci Eng A 1996;206:302-313.
- Harris AJ, et al. Development of High Temperature Nanoindentation Methodology and its Application in the Nanoindentation of Polycrystalline Tungsten in Vacuum to 950°C. Exp Mech 2017;57:1115-1126.
- Li J, et al. Study of nanoindentation mechanical response of nanocrystalline structures using molecular dynamics simulations. Appl Surf Sci 2016;364:190-200.
- Gerberich WW, et al. Indentation induced dislocation nucleation: the initial yield point. Acta Materialia 1996;44:3585-3598.
- Volinsky A and Gerberich WW. Nanoindentation techniques for assessing mechanical reliability at the nanoscale. Microelectronic Eng 2003;69:519-527.
- Weertman JR, et al. Structure and mechanical behavior of bulk nanocrystalline materials. MRS Bull 1999;24:44-53.
- Nix W. Mechanical properties of thin films. Metall Mater Trans A 1989;20:2217- 2245.
- Briscoe BJ, et al. The effect of indenter geometry on the elastic response to indentation. J Phys D: Appl Phys 1999;27:1156-1162.
- Zhang Y, et al. A model of size effects in nanoindentation. J Mech Phys Solids 2006;54:1668-1686.
- Bressan JD, et al. Modeling of nanoindentation of bulk and thin film by finite element method. In Wear 2005;258:115-122.
- Zhang X, et al. A systematic molecular dynamics simulation study of temperature dependent bilayer structural properties. Biochim Biophys Acta 2014;1838:2520-2529.
- Tackerman M, et al. Ab-Initio Molecular-Dynamics Simulation of the Solvation and Transport of H3O+ and Oh- Ions in Water. J Phys Chem 1995;99:5749-5752.
- Hasnaoui A, et al. Interaction between dislocations and grain boundaries under an indenter – a molecular dynamics simulation. Acta Mater 2004;52:2251-2258.
- Kelchner CL, et al. Dislocation nucleation and defect structure during surface indentation. Phys Rev B 1998;58:11085-11088.
- Ruestes CJ, et al. Atomistic simulation of tantalum nanoindentation: Effects of indenter diameter, penetration velocity, and interatomic potentials on defect mechanisms and evolution. Mater Sci Eng A 2014;613:390-403.
- Hagelaar JHA, et al. Atomistic simulations of the formation and destruction of nanoindentation contacts in tungsten. Phys Rev B - Condensed Matter Mater Phys 2006;73.
- Goel S, et al. Twinning anisotropy of tantalum during nanoindentation. Mater Sci Eng A 2015;627:249-261.
- Lesar R. Introduction to Computational Materials Science. Cambridge University Press 2013.
- Tadmor E and Miller R. Modeling Materials. Cambridge University Press 2011.
- Daw MS and Baskes MI. Embedded-atom method–derivation and application to impurities, surfaces, and other defects in metals. Phys Rev B 1984;29:6443-6453.
- Finnis M. Interatomic Forces in Condensed Matter. Oxford University Press 2003;129-186.
- Wang J, et al. A modified W-W interatomic potential based on ab initio calculations. Model Simul Mater Sci Eng 2014;015004:22.
- Plimpton S. Fast Parallel Algorithms for Short-Range Molecular” Dynamics. J Comput Phys 1995;117:1-19.
- Egami T, et al. Structural defects in amorphous solids A computer simulation study. Philos Mag A 1980;41:883-901.
- Falter C and Zierau W. Determination of the high temperature bulk modulus from self-diffusion experiments demonstrated for tungsten. J Appl Phys 1980;51:2070.
- Naveen Kumar N, et al. Active slip systems in bcc iron during nanoindentation: A molecular dynamics study. Comput Mater Sci 2013;77:260-263.
- Imran M, et al. Dynamic characteristics of nanoindentation in Ni: A molecular dynamics simulation study Chinese Phys B 2012;21:116201.
- Mehrez H, et al. Conductance through a single atom. Phys Rev B: Condensed Matter 1997;55:R1981-R11981.
- Jeng YR, et al. Molecular dynamics studies of atomic-scale friction for roller-on-slab systems with different rolling–sliding conditions. Nanotechnology 2005;16:1941.
- Oliver WC and Pharr GM. An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. J Mater Res 1992;7:1564.
- Chengewi, et al. A Study of Mechanical Properties and Material Removal of Polycrystalline Tungsten via Nanoindentation and Nanoscratch. Adv Mater Res 2013;797:706-710.
- Dylan J Morris. Finite element analysis and experimental investigation of the Hertzian assumption on the characterization of initial plastic yield. J Mater Res 2009;24.
- Sanders PG, et al. Elastic and tensile behavior of nanocrystalline copper and palladium. Acta Mater 1997;45:4019-4025.
- Kai Zhou, et al. Effects of grain size and shape on mechanical properties of nanocrystalline copper investigated by molecular dynamics. Mater Sci Eng A 2014;615:92–97.
- Te-Hua FANG, et al. Molecular Dynamics Analysis of Effects of Velocity and Loading on the Nanoindentation. Jpn J Appl Phys 2002;41:L 1328-L 1331.