Thermal Conductivity of Silicon Thin Films Deposited On Porous Alumina by PECVD

Porous ceramic materials are used in several applications in many engineering and industrial fields namely filters and membranes, catalyst for biomaterials, cell electrodes, and acoustically bulk media. Porous anodic alumina films is an interesting material [1] for nanotechnology applications because of its unusual properties compared to the bulk counterparts [2]. Many works have been published relative to the deposition of porous aluminum films [3]. Different methods of film growth were used, as for example reactive sputtering [4] and low pressure metal-organic chemical vapor deposition [5]. Thermal conductivity of ceramics is of general interest, since it may significantly influence other properties such as thermal shock resistance and may exhibit certain features, in particular porosity dependence, analogous to other properties [6]. The prediction of their thermal properties by analytical or computer calculation is therefore of strong interest [7]. In this work we demonstrate the capability to grow porous aluminum layers (PAL) by electrochemical anodisation method; the anodizing process was done by varying the anodizing voltage between 250 to 400 mV. A crystalline silicone films are deposited on the PAL by a PECVD technique. We present a computational model to determine the thermal conductivity K using the photothermal deflection technique (PTD).


INTRODUCTION
Porous ceramic materials are used in several applications in many engineering and industrial fields namely filters and membranes, catalyst for biomaterials, cell electrodes, and acoustically bulk media.Porous anodic alumina films is an interesting material [1] for nanotechnology applications because of its unusual properties compared to the bulk counterparts [2] .Many works have been published relative to the deposition of porous aluminum films [3] .Different methods of film growth were used, as for example reactive sputtering [4] and low pressure metal-organic chemical vapor deposition [5] .Thermal conductivity of ceramics is of general interest, since it may significantly influence other properties such as thermal shock resistance and may exhibit certain features, in particular porosity dependence, analogous to other properties [6] .The prediction of their thermal properties by analytical or computer calculation is therefore of strong interest [7] .In this work we demonstrate the capability to grow porous aluminum layers (PAL) by electrochemical anodisation method; the anodizing process was done by varying the anodizing voltage between 250 to 400 mV.A crystalline silicone films are deposited on the PAL by a PECVD technique.We present a computational model to determine the thermal conductivity K using the photothermal deflection technique (PTD).

FILM PREPARATION
High-purity aluminum foil (99.997%), 0.25mm thick was used as a starting material.The cleaned samples were anodized during 25 min in a solution of diluted sulfuric acid with 66.66% H 2 SO 4 and 33.33% H 2 O 2 at room temperature and with five different anodization currents (250 mA, 300 mA, 350mA and 400 mA).On the surface, nc-Si films were deposited by PECVD technique [8] at 50°C using a gas mixture of silane and H2 at a total pressure of 0.5 mTorr.

PHOTOTHERMAL MEASUREMENTS
The experimental device [9] is shown in Figure 1.The PTD is a sensitive optical tool for material analysis ] .When a sample is irradiated with modulated and monochromatic beam radiation, the absorbed energy is converted into heat through different where n is the fluid refractive index, x 0 is the distance between probe beam and the sample surface, and L is the sample length.= is the Thermal diffusivity and F is the modulation frequency of the heating beam.We notice that deflection is proportional to the complex temperature T0 at the sample surface.This temperature is calculated by solving the one dimension heat equation in the sample, the backing and the Surrounding fluid (Figure 3) These equations are solved while taking into account of the boundary conditions at different interfaces.The obtained surface temperature is given by: All thermal and optical parameters that appear in the above expression are given.

PHOTOTHERMAL MEASUREMENTS
In order to determine the thermal conductivity evolutions with the anodization currents of porous alumina.We present in Figure 3a-3d the coincidence between the experimental and theoretical curves of the normalized amplitude of the photothermal signal versus the square-root modulation frequency for various porosity.These curves have the same behaviour, but we notice small difference in the slope at low and high frequencies, and also small shifts of the maximum.Thermal conductivity K of the Si incorporated in porous alumina was determined by fitting the experimental amplitude curves to the corresponding theoretical ones.We notice that the thermal conductivity decreases with the increasing of anodization currents.This behaviour comes from the presence of air inside the micropores.The sponge-like spherical or columnar morphology of micropores may also reduce the thermal transport and carrier diffusion process, clearly illustrated in Table 1.

CONCLUSION
We notice a smaller thermal conductivity value (K=11.5 W. m -1 .K -1 ) for the sample with 200 mV; it may be due to a thermal insulating effect.We remark that K decrease with anodisation currents.
e-ISSN:2321-6212 p-ISSN:2347-2278 17 RRJOMS | Volume 4 | Issue 2 | June, 2016 relaxation processes.The generated thermal wave diffuses in the material and in the surrounding fluid (CCl4).The temperature variations in the fluid lead to a refractive index gradient causing the deflection of a probe laser beam (He-Ne 4 mW) skimming the sample surface.This deflection is detected by a position photosensor linked to a lock in amplifier.The obtained photothermal signal has two compounds: amplitude and phase.The principle of this technique is shown in Figure 2. The probe beam deflection is given by f 0 L / n(dn / dt) T σ Ψ =

Table 1 .
Thermal conductivity of Si thin film deposited on Porous alumina at different anodisation currents