Effect of Alkaline and Earth Oxides on the Chemical Durability of Borosilicate Opal Glasses Opacified with P 2 O 5

This investigation is disclosed a type of borosilicate opal glasses that provide new compositions of borosilicate glasses, opacified with P2O5, which have high chemical durability and low thermal expansion coefficient, with the general composition SiO2 73.0, B2O3 11.70, Al2O3 3.30, P2O5 1.30, Na2O (9.6-(X+Y)), CaO (X=0.1-050) and BaO (Y=4.52.9)wt%. Effects of Na2O, CaO and BaO, which are available in glass, were examined in acidic, water and steam leaching, and alkaline corrosion. The results showed ideal properties which were dependent to the limited ratio of Na2O/ BaO + CaO. This research has been scaled-up in the laboratory successfully and has been registered as patent No. 49441 in 28 June 2008 in Iranian Innovations Organization.


INTRODUCTION
Kunkel (1630-1705) was the first invented borosilicate opacified opal glasses via adding small amounts of bore ash containing calcium phosphate to the glass batch.In addition, arsenates, particularly lead arsenate and other phosphates, have been evaluated to produce "opaque" and "milk" glasses.Usually, about 1-5% mass was sufficient, but occasionally much more has been added.The basic studies about the glasses opacified by phosphates were carried out in 1899-1925 [1,2,3] .Then, the dependence of opacification on heat treatment, effects of additives, and studying mechanism of opacification were studied thoroughly [4,5,6,7] .Vogel in 1964 carried out investigations on the perfectly transparent composition of a specific kind of glass close to the borosilicate glasses by adding CaO and P2O5. [1,3]10][11][12] Opal glass, resistant to thermal shock, begins to happen as the improved borosilicate glasses.The mean coefficient of linear thermal expansion of borosilicate opal glasses is the lowest among industrial multi-component glasses along with easy handling and satisfactory chemical durability. [6,7,10,11] Opfying with phosphate has numerous advantages for opals resistant to thermal shock.P2O5 does not volatilize from the molten, as fluoride ions which corrode refractories; then, the stability and the time of industrial furnace and refractory would be increased.The usage of this formulation has many advantages for the furnace and melting process.Heat resisting opal borosilicate glasses is used for bake ware and other applications, wherein heat resistance and white opal appearance are desired.
In commercial borosilicate glasses for kitchenware, there are some parts of artistic items in which all the pieces have the same thermal coefficient expansion, particularly those having a new luxury in multiple glasses.Furthermore, they would be suitable for coating as stable glass layer and metallic internal body of reservoir for chemical reaction with corrosive reagents in high temperatures.
In this research, a novel type of borosilicate opal glass is provided, with improved chemical and thermal durability characteristics.It has white appearance as a unique color.In the current study, as a systematic effort, effect of Na2O to BaO and CaO wt% ratio was considered on chemical durability and thermal coefficient expansion e-ISSN:2321-6212 p-ISSN:2347-2278 of borosilicate opal glasses which are opacified with phosphate.
Table 1: Chemical composition of glass specimens.
The batch for borosilicate opal glass mostly was contained the components that were added in very small amounts, e.g., sodium meta phosphate, calcium carbonate, and barium carbonate, which must be weighed very carefully.In order to ensure uniform distribution of these batches in laboratory scale, the total dry raw material was mixed in 250 g quantities, divided into some parts, gradually added to Pt crucible, and was melted in an electrical furnace by using a thermal program at 1250-1600 °C for 3 h.Then, the molten glass in the crucible was poured into a plate of Zn/Cu alloy moulds, transferred to an annealing furnace and annealed at 630 °C.
Crystalline and non-crystalline glass phases were identified by X-ray diffraction method (XRD).Thermal expansions and glass transition temperature were measured by dilatometry method.The density of samples was measured by Archimedes method [13] .The ISO procedure, designated as 695, 698,719 and 720, was used to determine the chemical durability of glasses in alkaline solutions, acidic solutions, water, and steam [14,15,16,17] .In alkaline and acidic resistance test, the resistances were calculated by the loss in mass per unit area of the glass (mg/dm 2 ) after 3 h immersion in a boiling alkaline aqueous solution.The same procedure was achieved for acidic resistance by immersion in a boiling aqueous solution for 6 h.In the hydrolytic resistance in water and steam, amount of alkali released into the water at 98 and 121 °C was measured after immersion through titration with hydrochloric acid solutions.

RESULTS AND DISCUSSION
The X-ray diffraction patterns of the first glass samples (1-7) and the specimens (01-06) are presented in Figure 1.One large and broad peak around 2θ=23º was observed in all of the patterns with similar amount and concentration.This feature is typical for opal glasses with amorphous nature, in which nucleation is incomplete.Phase separation is the reason for crystalline nucleation in these glasses and relates to CaO and BaO content with different polarizing effect (Ca 2+ >Ba 2+ ).
Effect of phosphate addition on nucleation has been observed in all of the samples.However, sample No.7 had amorphous phase with crystalline peak with low intensity.Since the amount of P2O5 influenced on the crystal nucleation, and the ratio of glassy to crystalline phase in this sample was more than the other samples, addition of phosphate and BaO in minimum amount has been effective in the formation of the nuclei in glassy parent phase.
In all the XRD patterns, the initiated region for crystallization was common.Sample 1, in comparison with other samples, showed lower initiating region for crystallization; thus, a quartet peak in this area was observed.However, other samples revealed the same region for crystalline peak 2θ values for similar observed broad and sharp peaks.The XRD pattern of No.06 specimen was unusual, thus the crystalline phase was diminished than the glassy phase, but the configuration of the pattern was similar to the other specimens.It seems that decreasing BaO content led to divers effects on the amorphous phase and ratio of Na2O, BaO, and CaO affected opacification.XRD patterns of sample 2 and 5 were adapted, without any differences, because the ratio of Na2O to CaO and BaO in No.2 (0.03) was more than No. 5 In sample No. 7, the ratio of amorphous to crystalline phase was higher than in other samples, due to the minimum amounts of P2O5 and BaO.Meanwhile, the weakest crystallization was observed in No. 3 including high content of Al2O3.In the presence of minimum amount of BaO, crystalline phase was decreased, although crystal nucleation was occurred.This trend was probably due to the minimum amount of BaO and maximum amount of CaO.Because of higher content of phosphate, initiated region for crystallization in glassy phase was nearly the same in the samples 1 and 6.These samples had little similarity to sample 5, because Al2O3 was effective in crystal formation and immiscibility; however, the rate of crystallization was dependent on the BaO and CaO contents. [18]In the case of sample 3, in comparison with other parents, significant peaks were wide and weak.This observation would probably due to the high content of Al2O3.In comparison with patterns in specimens, a small shift in peak was observed, probably due to the presence of high content of CaO and low content of BaO.These amounts cause decreasing initial crystallization and less intense peaks.On the other hand, crystal growth in No.02 was more satisfactory and the significant peak was broader than in the other samples.In a short study of the influence of heating on glass, it was revealed that improving of the crystalline phase was independent to the heating range.Thermal expansion was affected by thermal history, so similar thermal conditions were used for all of the samples. [14]Tables 2-5 show some thermal expansion characteristics of samples and specimens.Among glass samples in Table 2, No.3 with Kα=3.2071×10 -6 K -1 and Kα=3.5938×10 -6 K -1 had minimum and maximum values, respectively, for thermal coefficient expansion.Moreover, Tg (glass transition temperature), Ts (softening point temperature), and Ts-Tg values for No.3 were the least.However, glass specimens showed different patterns and Kα values were increased with decreasing Tg (Table 3).
The ratios of Na2O to BaO and CaO for sample No.3 were similar to No.1 and 2; however, the contents of Al2O3, B2O3 and P2O5 were mainly different.Kα values in samples 3 and 7 were low; it seems that addition of Al2O3 and B2O3 significantly affected improving thermal coefficient expansion.Due to the fixed Al2O3, B2O3 and P2O5 contents in glass specimens, little differences in Kα values were observed.One of the most important thermal parameters which are found in this study would be the direct relation of Kα with Tg-Ts.The samples and specimens involving the lowest difference between Tg and Ts, showed the lowest thermal coefficient expansion, due to the minimum phase separation.The ratio content of α -/α with 10 ºC above and below Tg were collected for samples and specimens borosilicate opal glasses in Tables 4 and 5.The ratio content of α -/α was increased with decreasing Kα in specimens (01-06) and in samples.The coefficient thermal expansion was increased with widening of temperature range, 25-200, 25-300,25-400, 25-500, 25-570 ºC, etc; this increase was again approximately linear.This phenomenon was therefore characteristic for 3.3 glasses and borosilicate opal glasses that were prepared in this investigation.The chemical stability and durability of borosilicate opal glasses were affected by the chemical composition of the crystalline phase.Alkali metal ions were much more stable in the crystalline phase and rapidly were removed from the glass phase during the action of water on glasses [15,16,19,20] .This process was intensified by increasing temperature, the results showed leaching at 98 ºC and sterilization in 121 ºC [17,19,21,22] .Water and steam behaved according to the diffusion phenomenon. 19Hydrolytic resistance observed at 98 and 121 ºC, as depicted in figures 2 and 3 for the glass samples (1-7) and the specimens (01-06).Glass samples No. 6 and 4 revealed maximum HGB obtained and mass of sodium oxide per gram of glass grains were 89 and 160 (Na2O) µg/g of glass, respectively.The glass specimens of No. 01 and 03 had minimum and maximum values and their HGB were obtained with 90 and 124 µg of Na2O per each gram of glass, respectively.For better describing of alkaline oxide in specimens, three categories per value of Na2O/ BaO+CaO wt% were considered.Results showed that the HGB value was increased as a function of alkaline ratio (Figure 6) with a smooth slope; and HGA value was decreased as a function of alkaline ratio in (Figure 7).mg/dm 2 with a little difference of loss in mass per total surface area, respectively, were categorized in class A-1.In comparison with borosilicate glasses, these results showed high durability in alkaline solution for borosilicate opal glasses, so they would have more applications in industry.Similarly, results of acidic resistance for glass samples and specimens are exhibited in Figures 10 and 11 as grade S (mg/dm 2 ).The glass specimens of No.06 and 04 showed minimum and maximum values, and the S was obtained with 0.5 and 2.1, respectively; therefore, they should be included in S class 1 and 3.In addition, specimens No.01, 02, 03 with 1.0, 0.9, 1.0 mg/dm 2 , respectively, were in class 2.      Values of densities for the first glass samples were nearly the same (approximately 0.09 more than 3.3 glasses), and for glass specimens, this quantity averaged between 2.33-2.36,which is extended with the ratio of Na2O/BaO+CaO.In all XRD patterns, crystallite or other crystalline phases of SiO2 was very unfavorable to be existed; thus, identification of a meaningful relation between Tg-Ts and phase separation was impossible.Moreover, differences between Tg and Ts in these results did not affect the chemical durability.

CONCLUSION
In order to produce borosilicate opal glasses with ideal chemical resistance, it is necessary that the ratio of R2O and RO be limited and do not contain high concentrations of alkaline oxides in particular.However, all conditions should be controlled and other oxide ratios should be constant.Therefore, the glass does not affected by the heat treatment or any changes in the processing conditions.Observation of phase separation in the opal borosilicate glass confirms existence of crystals, which can react with water, alkaline, and/or acidic solutions; so that, the product would be unstable in this condition and chemical durability would be lowered down.However, in this investigation, under the identified conditions, chemical composition of crystalline phases was lowered down; thus, high chemical durability and high stability in leaching and corrosive solutions were obtained.
It seems that addition of Al2O3 and B2O3 has significantly affected improving of thermal coefficient expansion.Direct relation between Kα and |Tg-Ts| proved that the samples and specimens were contained the lowest difference between Tg and Ts and the lowest thermal coefficient expansion obtained, due to the least phase separation.
The value of P2O5 influenced the crystal nucleation; in addition, phosphate and BaO in minimum value were effective in the formation of nuclei in glassy parent phase.Undoubtedly, the initiating role of P2O5 was necessary for crystallization and low values of P2O5 decreased the density of opacity, similar to the opaque glasses.BaO in 0.8 wt% was the minimum content which was needed for initial crystallization.BaO showed divers effects on amorphous phase and it was effective on opacification.All of these results showed that there are clear relation between the ratio of Na2O, BaO and CaO.
Al2O3 was effective in crystal formation and immiscibility, but the rate of crystallization was dependent on the BaO and CaO contents.When 5 wt% of alumina was added, initiating of crystallization and size of the crystals were changed.

Figure 3 :
Figure 3: HGB for glass specimens at 98 ºC.The glass samples of No.6 and 5 have minimum and maximum values for water resistance, respectively, and accomplished HGB with 1001 and 1032 µg of Na2O per each gram of glass grains, respectively (Figures4 and 5).The glass specimens No.05 and 01 as minimum and maximum values, showed HGA with 900 and 990 µg of Na2O per each gram of glass, respectively.

Figure 4 :
Figure 4: Variation of hydrolytic resistances of the samples in 121 ºC.

Figure 5 :
Figure 5: Variations of hydrolytic resistances of the specimens in 121 ºC.

Figure 7 :
Figure 7: HGA values against Na2O/ BaO+CaO for the specimens.Variation of alkaline resistance in glass samples and specimens are shown in Figures 8 and 9.The glass samples of No.4 and 7 showed minimum and maximum values, respectively.The A (or LBK) was obtained through removal of glass thin plate 11.0 and 30.0 mg/dm 2 , respectively, and the other values for the selected samples were 21.1, 21.2, 22.0, 26.4 and 25.1, mg/dm 2 .These are included in A class1or in LBK class1, because of alkaline solutions had slight attack and weight loss are lower than 75 mg/dm 2 .In the glass specimens of No.05 and 06, as minimum and maximum values, A was obtained with 0.9 and 25.0 mg/dm 2 , respectively, and are . The glass samples of No.4 and 7 showed minimum and maximum values, respectively.The A (or LBK) was obtained through removal of glass thin plate 11.0 and 30.0 mg/dm 2 , respectively, and the other values for the selected samples were 21.1, 21.2, 22.0, 26.4 and 25.1, mg/dm 2 .These are included in A class1or in LBK class1, because of alkaline solutions had slight attack and weight loss are lower than 75 mg/dm 2 .In the glass specimens of No.05 and 06, as minimum and maximum values, A was obtained with 0.9 and 25.0 mg/dm 2 , respectively, and are e-ISSN:2321-6212 p-ISSN:2347-2278 included in class A-1.In addition, specimens No.01, 03, 05, 06 and 07 with 11.4, 12.0, 11.7, 11.6 and 11.1

Figure 8 :
Figure 8: Alkaline resistance in the glass samples.Loss in mass per total surface area after 3h is depicted in Y axis.

Figure 9 :
Figure 9: Alkaline resistance in the specimens.Loss in mass per total surface area after 3h is depicted in Y axis.

Figure 10 :
Figure 10: Acidic resistance of the glass samples.Loss in mass per total surface area is depicted in Y axis.

Figure 11 :
Figure 11: Acidic resistance of the specimens.Loss in mass per total surface area is depicted in Y axis.The role of alkaline oxide in specimens in three categories for specimen's glasses is considered.Results showed the A values increased and the S values decreased as a function of alkaline ratio.The relation between resistance alkaline, acidic resistance, and Na2O/BaO+CaO ratio are shown in figures 12 and 13.

Figure 12 :
Figure 12: Alkaline resistant test as a function of Na2O/BaO+CaO.
. Moreover, P2O5 content in No.2 (0.34) was lower than in No.5; thus, differences in nucleation agent functioned similarly in glassy and crystalline phases.

Table 2 .
Mean coefficients of linear thermal expansion, Tg, Ts, Td and |Tg-Ts| of samples in the temperature range of 20-300 ºC.

Table 3 :
Mean coefficients of linear thermal expansion, Tg, Ts, Td and |Tg-Ts| of specimens in the temperature range 20-300 ºC.

Table 4 :
The ratio of  -/ with 10 ºC above and below Tg for the samples.

Table 5 :
The ratio of α -/α with 10 ºC above and below Tg for the samples.